催化剂及助剂

三烯丙基异氰脲酸酯

产品名称:三烯丙基异氰脲酸酯

CAS:1025-15-6

别名：促进剂TAIC,过氧化物助交联剂;交联剂TAIC(粉);1,3,5-三烯丙基-均三嗪-2,4,6-三酮;TAIC粉剂;三烯丙基异三聚氰酸酯(TAIC);三烯丙基异氰脲酸酯/三烯丙基-S-三嗪-2,4,6(1H,3H,5H)-三酮;1,3,5-三烯丙基-1,3,5-三嗪-2,4,6(1H,3H,5H)三酮;1,3,5-三烯丙基-1,3,5-三嗪-2,4,6(1H,3H,5H)三酮,含稳定剂MEHQ

英文名：1,3,5-Tri-2-propenyl-1,3,5-triazine-2,4,6(1H,3H,5H)-trione

熔点 20.5°C
沸点 149-152 °C4 mm Hg(lit.)
密度 1.159 g/mL at 25 °C(lit.)
折射率 n20/D 1.513(lit.)
闪点 >230 °F
储存条件 2-8°C
溶解度 3.7g/l
形态Liquid After Melting
颜色Clear colorless to yellow
水溶解性 > 1 g/L (20 ºC)
稳定性May be prone to spontaneous polymerization. Commercial product is generally supllied with added stabilizer such as t-butylhydroquinone. Incompatible with peroxides, strong oxidizing agents, strong acids, strong bases.
InChIKeyKOMNUTZXSVSERR-UHFFFAOYSA-N
CAS 数据库1025-15-6(CAS DataBase Reference)
NIST化学物质信息1,3,5-Triazine-2,4,6(1H,3H,5H)-trione, 1,3,5-tri-2-propenyl-(1025-15-6)
EPA化学物质信息1,3,5-Triazine-2, 4,6(1H,3H,5H)-trione, 1,3,5-tri-2-propenyl-(1025-15-6)

用途用作聚烯烃的交联和改性剂、特种橡胶的助硫化剂、不饱和聚酯玻璃钢的交联剂、聚苯乙烯的内增塑剂等
用途含芳香环的多功能烯烃单体，广泛用作多种热塑塑料，离子交换树脂，特种橡胶的交联剂、改性剂和助化剂。乙丙三元或二元=、=橡=、CPE、EVA等特种橡胶用TAIC作助硫化剂进行硫化（与DCP并用，一般用量为DCP2%TAIC3—4%）可显著地缩短硫化时间，提高制品的机械性、耐热性、耐候性和耐溶剂性等。
用途交联剂TAIC 是一种含芳杂环的多功能烯烃单体，主要用于多种用途的交联剂和改性剂。
用途 TAIC是一种含芳杂环的多功能烯烃单体，广泛用于多种热塑塑料、离子交换树脂、特种橡胶的交联剂、改性剂和助硫化剂等，以及光固化涂料、光敏抗蚀剂、阻燃剂等的中间体，是一种用途十分广泛的新型高分子材料的助剂。
用途 1。可作橡胶和塑料的助交联剂和辅照助交联剂,对提高交联度，降低辐照剂量，卓有成效。 2。对乙丙橡胶、氯化聚乙烯、聚烯烃等以过氧化物为硫化剂时TAIC是良好的助硫化剂。 3。对PVC的辐照交联有一定的敏化作用，可作为光辐射交联剂或光敏剂。 4。过氧化物固化反应的偶合剂。 5。由于TAIC均聚物的交联密度较大，它被广泛用于胶粘剂、电缆、纸张和有机玻璃的工业生产，以增强其他基质在聚合过程中的强度。 2.过氧化物固化反应的偶合剂。 3.由于TAIC均聚物的交联密度较大，它被广泛用于胶粘剂、电缆、纸张和有机玻璃的工
用途 1）.聚烯烃的交联和改性：4.5聚乙烯、聚丙烯、聚氯乙烯、聚苯乙稀的交联和改性,可提高耐热性、机械强度、耐腐蚀、耐溶剂等。2）.特种橡胶的助硫化：乙丙的二元或三元胶、氟橡胶、硅橡胶、聚氨脂等特种橡胶,用TAIC作助硫化剂进行硫化(DCP并用),一般用量为0.5-3%可显著缩短硫化时间,提高机械性能、耐磨性、耐候性和耐溶剂。3）.不饱和聚酯玻璃钢的交联剂：热压不饱和聚脂玻璃钢用少量TAIC作交联剂可显著提高耐热性和机械强度,耐热性可提高到200℃以上。4）.聚苯乙稀的内增塑剂：与TAIC进行共聚反
用途用作交联剂和改性剂

上一篇：防老剂DPC-34 下一篇：离子交换树酯